HYSOL KL1000-4T电子胶水/塑封胶水/汉高乐泰胶水/塑封方案

技术服务热线：021-51693135 / 021-22818476

乐泰 HYSOL KL 1000-4T provides the lowest cost ofownership with superior moldability and reliability.
This materialis designed to achieve JEDEC Level 4 requirements, at 220°C reflow temperature.
乐泰 HYSOL KL 1000-4T meets UL 94 V-0 Flammabilityat 3.175mm thickness.
TYPICAL PROPERTIES OF UNCURED MATERIALGel Time @ 175 °C, seconds 23 Spiral Flow, @ 175°C, cm 85Shelf Life:@ 5oC, days 365TYPICAL PROCESS DATAHandling Preheat Temperature :Conventional mold, °C 80 to 100Automold, seconds 0 to 5Molding Temperature, °C 150 to 195Molding Pressure, Kg/cm2 40 to 100Transfer Time:Conventional mold, seconds 10 to 20Automold, seconds 4 to 10Curing Time, @ 175oC:Conventional mold, seconds 60 to 120Automold, seconds 50 to 80Post Cure @ 175°C, hours 4 to 6乐泰 HYSOL KL 1000-4T has been formulated to provide thebest possible moldability and as wide a molding latitude as possible.
Although molding and curing conditions will vary from situation tosituation, recommended starting ranges are shown aboveStorageStore product in the unopened container in a dry location.Storage information may be indicated on the product containerlabeling.
Powder Storage - Powder or preforms should be stored at 5oCor below, in closed containers.
After removal from coldstorage, the material MUST be allowed to come to roomtemperature, in the sealed container, to avoid moisturecontamination.
The suggested waiting time for a standard 15kg carton box is 24 hours.

乐泰 HYSOL KL 1000-4T提供*低的拥有成本，具有出色的成型性和可靠性。
这种材料设计用于在220°C达到JEDEC 4级要求回流温度.乐泰 HYSOL KL 1000-4T满足UL 94 V-0 Flammabilityat 3.175mm厚度。
固化材料的特性特性时间@ 175°C秒秒23螺旋流，@ 175°C，cm 85Shelf寿命：@5oC，天365工艺流程数据处理预热温度：常规模具，°C 80至100Automold，秒0至5模具温度，℃150至195模压，Kg /cm240至100转印时间：常规模具秒10至20Auoldold秒秒4至10℃恒定时间@ 175℃：常规模具，秒60至120Automold，秒50至80固化@ 175°C，小时4至6乐泰 HYSOL KL 1000-4T已经配制，以提供尽可能*高的成型性和更宽的成型纬度。